Material |
N/AType 321 Stainless Steel |
Shapeform |
N/ASheets |
Thickness |
N/A16 gauge |
Thickness |
N/A0.060 inches1.524 mm |
Size |
N/A36 x 120 |
Width |
N/A36 |
Length |
N/A120 |
Sheet Weight per Unit Area |
N/A2.520 lbs/ft²12.30264 kg/m² |
Estimated Weight per Sheet |
N/A75.61 lbs34.25133 kg |
Finish |
N/ANo. 2D |
Condition |
N/ACold Rolled Annealed |
Nominal Composition |
N/A0.08% Max. Carbon1.00% Max. Silicon17.00 to 20.00% Chrominum2.00% Max. Manganese34.00 to 37.00% Nickel |
ASTM Specification |
N/AASTM A240ASTM A480ASTM SA-240UNS S31008 |
Steel Alloy Group |
N/AAustenitic |
Magnetic Properties |
N/ANon-Magnetic |
Harden By |
N/ACold Work |
Corrosion Resistance |
N/AHigh |
Hardness |
N/ALow to Med. |
Strength |
N/ALow to Med. |
Ductility |
N/AHigh |
Toughness |
N/ALow |
Elec. Conductance |
N/ALow |
Thermal Conductance |
N/ALow |
Thermal Expansion |
N/AHigh |
Heat Resistance (Scaling Strength) |
N/AHigh/High |
Yield Strength |
N/A31000 lbs/in² |
Tensile Strength |
N/A79000 lbs/in² |
Elongation percent in 2 inches |
N/A58 % |
Hardness (Rockwell B) |
N/A72 |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F |
N/A18000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F |
N/A13000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F |
N/A8700 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F |
N/A4500 lbs/in² |
Density |
N/A0.29 lbs/in³ |
Modulus of Elasticity in Tension |
N/A28.0 x 106lbs/in² |
Specific Heat (32 to 212°F) |
N/A0.12 BTU/ºF/lbs |
Thermal Conductivity at 212°F |
N/A9.3 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F |
N/A12.8 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) |
N/A9.3 x 10-6ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) |
N/A9.5 x 10-6ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) |
N/A10.3 x 10-6ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) |
N/A10.7 x 10-6ºF |
Melting Point Range |
N/A2550 to 2600 ºF |
Electrical Resistivity |
N/A72 µΩ.cm |
Max. Operating Temp. (Continuous Service) |
N/A1650 ºF |
Max. Operating Temp. (Intermittent Service) |
N/A1500 ºF |
Welding Properties |
N/AVery Good-Tough Welds |
Drawing and Stamping |
N/AGood |
Hot Working - Initial Forging |
N/A2100 to 2300 ºF |
Annealing Temp. |
N/A1750 to 2050 ºF |
Stress Relieving Temp. |
N/A400 to 750 ºF |
N/A
|