6063 grade is commonly referred to as the architectural alloy. It was developed as an extrusion alloy with relatively high tensile properties, excellent finishing characteristics and a high degree of resistance to corrosion. This alloy is most often found in various interior and exterior architectural applications, such as windows, doors, store fronts and assorted trim items. It is the alloy best suited for anodizing applications - either plain or in a variety of colors.

6063-752
Extruded Stock Lengths 21' 1" (Sharp Inside and Outside Corners)
AMS-QQ-A-200/9
测量单位

Specifications

Material

N/AAluminum

Shapeform

N/A方管

系列

N/A6063-T52

年级

N/A6063

Temper

N/AT52

Size

N/A1 3/4 x 1 3/4 x 0.125 inches

工作十进制等效

N/A1.750 x 1.750 x 0.125 inches44.45 x 44.45 x 3.175毫米

宽度

N/A1 3/4 inches

Length

N/A1 3/4 inches

高度

N/A0.125英寸

Weight

N/A0.9458磅/英尺1.4075055112 kg/m

估计重量

N/A19.941磅9.0452376公斤

估计重量24'

N/AAMS-QQ-A-200/9

Density

N/A0.097 lbs/in³

Specific Gravity

N/A2.70

Typical Mechanical Properties

Ultimate Strength

N/A27 KSI

Yield Strength

N/A21 ksi

2英寸的伸长百分比

N/A12

Hardness Brinnel Number

N/A60

终极剪切强度

N/A17 ksi
Fatigue Endurance Limit1 N/A10 ksi
Modulus of Elasticity2 N/A10.0 x 103ksi

Comparative Characteristics and Applications

对腐蚀的抗性 - 一般3 N/AA

应力腐蚀破裂

N/AA

Workability (Cold)

N/AB

Mechinability

N/AC
Brazeability4 N/AA
气焊性5 N/AA
Arc Weldability6 N/AA
Resistance Spot and Seam Weldability7 N/AA

Applications

N/A管道栏杆,家具,建筑挤压

铝合金名称

N/A

    The aluminum industry uses a four-digit index system for the designation of its wrought aluminum alloys.
    As outlined below, the first digit indicates the alloy group according to the major alloying elements.

    1xxx Series
    In this group minimum aluminum content is 99% and there is no major alloying element. The second digit indicates modifications in impurity limits. If the second digit is zero, there is no special control on individual impurities. Digits 1 through 9, which are assigned consecutively as needed, indicate special control of one or more individual impurities. The last two digits indicate specific minimum aluminum content. Although the absolute minimum aluminum content in this group is 99%, the minimum for certain grades is higher than 99%, and the last two digits represent the hundredths of a per cent over 99. Thus, 1030 would indicate 99.30% minimum aluminum. without special control on individual impurities. The designations 1130, 1230, 1330, etc.. indicate the same purity with special control on one or more impurities. Likewise 1100 indicates minimum aluminum content of 99.00% with individual impurity control.

    2xxx至9xxx系列
    The major alloying elements are indicated by the first digit, as follows:
      2xxx Copper
      3xxx Manganese
      4xxx Silicon
      5xxx Magnesium
      6xxx Magnesium and silicon
      7xxx Zinc
      8xxx Other element
      9xxx Unused series

    第二个数字表示合金修饰。如果第二位数为零。它指示原始合金:数字1至9,连续分配,指示合金修饰。最后两个数字没有特殊的意义,仅用于识别该组中的不同合金。

    实验合金
    实验合金是根据四位数系统指定的,但是它们的前缀为字母X。当合金成为标准配合时,前缀被删除。在开发过程中,在将它们指定为实验之前,新合金由其发起人分配的序列号确定。分配X号时停用序列号的使用。

  • 1Based on 500,000.000 cycles of completely reversed stress using the R. R. Moore-type of machine and specimen.
  • 2Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus.
  • 3基于间歇性喷涂或浸入,基于对氯化钠溶液的暴露,等级A至E是优异顺序的相对评分。具有A和B等级的合金可以在没有保护的情况下用于工业和海岸氛围。具有C,D和E等级的合金通常应至少在Faying表面上受到保护。
  • 4Ratings A through D for Weldability and Brazeability are relative ratings.
  • 5A = Generally weldable by all commercial procedures and methods.
    B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
    C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.
  • 6A = Generally weldable by all commercial procedures and methods.
    B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
    C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.
  • 7A = Generally weldable by all commercial procedures and methods.
    B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
    C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.